Trowel plastering machine
![]()
Format: Powder
Yield: 4.40 kg/m² per cm thickness (±10%), 0.90 lb/ft² per inch thickness (±10%)
Density: 450 kg/m³ (±10%), 28.09 lb/ft³ (±0.62%)
Grain size: 0–3 mm, 0 – 0.11 in
Application temperature: +5°C to +30°C (+41°F to +95°F)
Thickness: Minimum 1.5 cm, maximum 2.5 cm (2 cm for ceilings)
Drying time (T=23°C; U.R. 50%) : 15 days
Fire reaction: Euroclass A1
Compressive Strength: 5.1 N/mm² (739.69 lbf/in² (psi))
Flexural strength: 1.4 N/mm² (203.05 lbf/in² (psi))
Dried mortar porosity: 71.64%(17.83% macroporosity and 54.94% microporosity)
Vapour permeability coefficient (µ): µ = 4/WVT = 14 grains/h·ft²
Thermal conductivity: 0.08 W/mK
Thermal resistance (R) for 1 cm/ 0.4 in thickness: 0.125 m²K/W
Adhesion onto the support (brick): 0.258 MPa = N/mm² U
Storage: 18 months
Packaging: 20 kg (44 lb) paper bag
Yield: 4.40 kg/m² per cm thickness (±10%), 0.90 lb/ft² per inch thickness (±10%)
Density: 450 kg/m³ (±10%), 28.09 lb/ft³ (±0.62%)
Grain size: 0–3 mm, 0 – 0.11 in
Application temperature: +5°C to +30°C (+41°F to +95°F)
Thickness: Minimum 1.5 cm, maximum 2.5 cm (2 cm for ceilings)
Drying time (T=23°C; U.R. 50%) : 15 days
Fire reaction: Euroclass A1
Compressive Strength: 5.1 N/mm² (739.69 lbf/in² (psi))
Flexural strength: 1.4 N/mm² (203.05 lbf/in² (psi))
Dried mortar porosity: 71.64%(17.83% macroporosity and 54.94% microporosity)
Vapour permeability coefficient (µ): µ = 4/WVT = 14 grains/h·ft²
Thermal conductivity: 0.08 W/mK
Thermal resistance (R) for 1 cm/ 0.4 in thickness: 0.125 m²K/W
Adhesion onto the support (brick): 0.258 MPa = N/mm² U
Storage: 18 months
Packaging: 20 kg (44 lb) paper bag
Diathonite-Deumix-Technical data sheet